专注于自动化焊割设备制造
浏览数量： 0 作者： 本站编辑 发布时间： 2025-10-22 来源： 本站
| 激光器型号 | RFL-60000(150u) | 切割头光学配比 | 准直100/聚焦300 | |||||||
| 材料 | 厚度[mm] | 速度[m/min] | 功率 [W] | 气体 | 校正后气压 [bar] | 喷嘴[mm] | 焦点位置 [mm] | 切割高度[mm] | 频率[HZ] | 占空比[%] |
| 碳钢 | 20 | 7.5-8.5 | 40000~60000 | N₂＆O₂ | 4 | 6.0B | -6 | 0.3 | ||
| 25 | 5.5-6.5 | 4 | 6.0B | -9 | 0.3 | |||||
| 30 | 4-5.5 | 4 | 6.0B | -12 | 0.3 | |||||
| 35 | 3-4.5 | 3 | 6.0B | -17.5 | 0.3 | |||||
| 40 | 2.5-3.5 | 3 | 10.0B | -19 | 0.3 | |||||
| 碳钢 | 16 | 1.6-1.8 | 12000 | O₂ 正焦 | 0.5 | 1.4SP | +15 | 0.3 | ||
| 18 | 1.6-1.7 | 0.55 | 1.4SP | +16 | 0.3 | |||||
| 20 | 1.5-1.6 | 0.6 | 1.6SP | +18 | 0.3 | |||||
| 25 | 1.2-1.4 | 20000 | 0.6 | 1.6SP | +18 | 0.3 | ||||
| 30 | 1.2-1.3 | 0.65 | 1.8SP | +21 | 0.3 | |||||
| 35 | 1.1-1.2 | 0.8 | 1.8SP | +21 | 0.3 | |||||
| 40 | 0.9-1.1 | 25000 | 0.9 | 1.8SP | +21 | 0.3 | ||||
| 45 | 0.8-1 | 1.1 | 1.8SP | +21 | 0.3 | |||||
| 50 | 0.75-0.9 | 30000 | 0.85 | 2.3SP | +26 | 0.3 | ||||
| 60 | 0.7-0.8 | 50000 | 0.8 | 3.0S | +30 | 0.3 | ||||
| 70 | 0.6-0.8 | 60000 | 1.2 | 3.0S | +35 | 0.3 | ||||
| 80 | 0.6-0.7 | 1 | 3.5S | +39 | 0.3 | |||||
| 100 | 0.5-0.6 | 1 | 4.0S | +45 | 0.3 | |||||
| 160 | 0.15-0.25 | 1.5 | 4.0S | +45 | 5 | |||||
| 200 | 0.15-0.2 | 1.5 | 4.0S | +45 | 3 | |||||
| 碳钢 | 20 | 2.2-2.5 | 20000 | O₂ 负焦 | 1.5 | 1.8SP | -14 | 1.5 | ||
| 25 | 1.8-2 | 20000 | 1.3 | 2.0SP | -16 | 1.5 | ||||
| 30 | 1.6-1.8 | 20000 | 1.5 | 2.0SP | -17 | 1.5 | ||||
| 35 | 1.4-1.6 | 26000 | 1.8 | 2.0SP | -17 | 1.5 | ||||
| 40 | 1.1-1.4 | 26000 | 1.4 | 2.5SP | -19 | 3 | ||||
| 50 | 1.1-1.3 | 30000~40000 | 1 | 2.5SP | -22 | 3 | ||||
| 60 | 1-1.3 | 40000~60000 | 1 | 3.0S | -30 | 3.5 | ||||
| 70 | 0.9-1.2 | 1 | 3.0S | -30 | 3.5 | |||||
| 80 | 0.8-1 | 1 | 3.0S | -33 | 4 | |||||
| 100 | 0.5-0.65 | 1.1 | 3.5S | -40 | 4 | |||||
| 不锈钢 | 20 | 7-9 | 50000~60000 | Air | 8 | 6.0B | -8 | 0.3 | ||
| 25 | 5.5-6.5 | 3 | 8.0B | -11 | 0.3 | |||||
| 30 | 4-5.5 | 3 | 8.0B | -13 | 0.3 | |||||
| 35 | 3.5-4.5 | 3 | 8.0B | -18 | 0.3 | |||||
| 40 | 2.5-3.5 | 4 | 8.0B | -18 | 0.3 | |||||
| 50 | 1.6-2 | 4 | 10.0B | -28 | 0.3 | |||||
| 60 | 1.3-1.6 | 3 | 10.0B | -33 | 0.3 | |||||
| 65 | 1-1.2 | 3 | 10.0B | -35 | 0.3 | |||||
| 70 | 0.8-1 | 3 | 10.0B | -39 | 0.3 | |||||
| 80 | 0.5-0.7 | 3 | 10.0B | -42 | 0.3 | |||||
| 90 | 0.4-0.5 | 3 | 10.0B | -40 | 0.3 | |||||
| 90(调制） | 0.2-0.25 | 3 | 10.0B | -40 | 0.3 | 100~200 | 45~55 | |||
| 100 | 0.3-0.5 | 3 | 10.0B | -50 | 0.3 | |||||
| 100(调制） | 0.15-0.2 | 3 | 10.0B | -37 | 0.3 | 50~100 | 45~55 | |||
| 120 | 0.2-0.3 | 3 | 10.0B | -45 | 0.3 | |||||
| 130 | 0.18-0.25 | 3 | 10.0B | -50 | 0.3 | |||||
| 140 | 0.15-0.2 | 3 | 10.0B | -57 | 0.3 | |||||
| 150 | 0.12-0.15 | 3 | 10.0B | -65 | 0.3 | |||||
| 备注：表中红标参数为打样参数，在实际加工中受各类因素影响较大，仅适合小批量生产，不推荐大批量生产加工，建议使用更高功率激光器。 | ||||||||||